- Phase Transformation at High Temperatures and Coercivity of Sm-Co-Cu-Fe Magnet Alloys
- Sm Co Cu Feケイ ジシャク ゴウキン ノ コウオン ニ
この論文をさがす
説明
It is well known that Sm(Co,Cu,Fe)z (Z=near 7) alloys containing a proper quantity of Cu and Fe possess high coercivity and are used as superior permanent magnet materials. The Sm-Co-Cu-Fe quaternary phase diagram has not been studied. Therefore, the phase diagram near compositions of magnet alloys, and furthermore, relationships between phase transformations at high temperatures and coercivities were investigated. That is, Sm-Co-13 at%Cu-10 at%Fe and Sm-Co-9 at%Cu-18 at%Fe sections of the phase diagram were determined in the Sm content range from 10 to 15 at%. Furthermore, for various Sm(Co,Cu,Fe)z (Z=near 7) alloys, relationships between crystal structures after homogenizing treatment and coercivities after aging treatment were examined. The results are summarized as follows:<BR>(1) The Sm2(Co,Cu,Fe)17 intermetallic compound (2/17 phase) has solubility from 10.5 to about 13.0 at%Sm at high temperatures. In the extended homogeneity region, the 2/17 phase possesses the hexagonal TbCu7 structure or the rhombohedral Th2Zn17 structure depending on the quantity of Cu and Fe. The limits of the former compositions are given by approximately 16≤Cu(at%)+0.73Fe(at%)≤23 and Cu(at%)+3>Fe(at%).<BR>(2) The Sm(Co,Cu,Fe)z (Z=near 7) alloys quenched after homogenizing treatment, by which the 2/17 phase with TbCu7 structure is obtained, can possess high coercivity after the aging treatment.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 50 (2), 235-241, 1986
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681462874752
-
- NII論文ID
- 130007340288
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
-
- NDL書誌ID
- 3070344
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可