Sulfur and nitrogen distributions during coal carbonization and the influence s of these elements on coal fluidity
-
- Tsubouchi Naoto
- Center for Advanced Research of Energy and Materials, Hokkaido University,
-
- Mochizuki Yuuki
- Center for Advanced Research of Energy and Materials, Hokkaido University,
-
- Ono Yohei
- Sakaide Plant, Mitsubishi Chemical Corporation
-
- Uebo Kazuya
- Technical Research & Development Bureau, Nippon Steel & Sumitomo Metal Corporation
-
- Takanohashi Toshimasa
- Energy Technology Research Institute, National Institute of Advanced Industrial Science and Technology
-
- Sakimoto Naoto
- Energy Technology Research Institute, National Institute of Advanced Industrial Science and Technology
書誌事項
- タイトル別名
-
- Sulfur and Nitrogen Distributions during Coal Carbonization and the Influences of These Elements on Coal Fluidity and Coke Strength
この論文をさがす
説明
The present study focuses on examining the fate of coal-S and coal-N during carbonization in detail and making clear the effects of these elements on coal fluidity and coke strength. When eight kinds of caking coals with 80–88 mass%-daf C are carbonized in high-purity He at 3°C/min up to 1000°C with a quartz-made fixed bed reactor, 50–75% of coal-S remains as FeS and organic-S in the coke, and the rest is released as tar-S and H2S. Most of coal-N is also retained in the coke, and the remainder is converted to tar-N, HCN, NH3 and N2. The eight coals give Gieseler maximum fluidity values between 435 and 480°C, and the value tends to be larger at a smaller sulfur content in coal or in the carbonaceous material recovered after carbonization at 450°C. It also seems that the value increases with increasing nitrogen content in coal or total amount of either HCN or NH3 formed up to 450°C. Furthermore, the addition of S-containing compounds to an Australian bituminous coal lowers coal fluidity and coke strength considerably, whereas indole gives the reverse effect on them. On the basis of these results, it is suggested that coal-S or some coal-N has a negative or positive effect on the two properties, respectively.
収録刊行物
-
- ISIJ International
-
ISIJ International 54 (11), 2439-2445, 2014
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681463660160
-
- NII論文ID
- 130004704990
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BC2cXhvFymtrrK
-
- ISSN
- 13475460
- 09151559
-
- HANDLE
- 2115/79335
-
- 本文言語コード
- en
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- IRDB
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可