Attachment of Liquid Calcium Aluminate Inclusions on Inner Wall of Submerged Entry Nozzle during Continuous Casting of Calcium-Treated Steel
-
- Deng Zhiyin
- School of Materials and Metallurgy, Northeastern University Department of Materials Science and Engineering, KTH Royal Institute of Technology
-
- Zhu Miaoyong
- School of Materials and Metallurgy, Northeastern University
-
- Zhong Baojun
- Technology Center, Xingtai Iron & Steel Co. Ltd
-
- Sichen Du
- Department of Materials Science and Engineering, KTH Royal Institute of Technology
抄録
In the present study, inclusions in calcium-treated steel after RH treatment, in the tundish and in bloom were studied. Only two types of inclusions were detected in all steel samples, namely liquid calcium aluminate inclusions and inclusions of two phases with spinel in the center surrounded by the liquid calcium aluminate. The attachment of the inclusions on the inner surface of SEN was investigated for two types of refractory materials. The results indicated that liquid calcium aluminate inclusions could attach on the wall of SEN, when the refractory had big grain size and big cavities on the surface. On the other hand, tiny grain size and smooth surface of the SEN showed no attachment of the inclusions. The different behaviors of the two types of SEN were well explained using the results of flow calculation in the nozzle. The mechanism of the attachment was also discussed based on the experimental results and the CFD calculation. The tiny nodules formed on the surface of the inner nozzle due to inclusion attachment could be a source of macro inclusions.
収録刊行物
-
- ISIJ International
-
ISIJ International 54 (12), 2813-2820, 2014
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681465698432
-
- NII論文ID
- 130004734455
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可