Effect of Nitrogen Ion Implantation on Wettability of Partially Stabilized Zirconia with Molten Cu Alloys
-
- Iwamoto Nobuya
- Welding Research Institute, Osaka University
-
- Yokoo Hajime
- Development Department, Osaka Cement Co., Ltd.
-
- Inoue Hirofumi
- Welding Research Institute, Osaka University
Bibliographic Information
- Other Title
-
- 窒素イオンを注入した部分安定化ジルコニアの濡れ性
- チッソ イオン オ チュウニュウシタ ブブン アンテイカ ジルコニア ノ ヌレ
Search this article
Abstract
A partially stabilized zirconia (PSZ) was implanted with N+ ions and the wettability against the Zr-47 mass%Cu alloy was measured by the sessile drop method. Surface characterization of the implanted 3Y-PSZ was performed using XRD and XPS.<BR>The contact angle of PSZ against the Zr-47Cu alloy at 1273 K was improved from about 60 to 45 degrees by the implantation. The results of XRD showed that tetragonal phase of zirconia was converted to a monoclinic phase by the implantation. XPS indicated that the surface of the implanted PSZ was more metallic as compared with the inside of the material. This implies that zirconia was reduced by N+ ion implantation. The improvement of wettability is considered to be attributable to the formation of the metallic and active layer up on the surface.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 57 (3), 241-244, 1993
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681466265856
-
- NII Article ID
- 130007340383
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 3810575
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed