- Change of Cross-Sectional Shape of Sn-37 mass%Pb Alloy Fiber in the In-Rotating-Liquid-Spinning Process
- カイテンエキチュウ ボウシホウ ニ オケル Sn 37massパーセント P
この論文をさがす
説明
It is difficult to produce the continuous fiber of a low surface tension alloy with a round cross-section by using the In-Rotating-Liquid-Spinning process. The relation between the cross-sectional shape of the fiber and the spinning conditions has been examined by using a Sn-37 mass%Pb alloy. The mean mass flow rate of molten metal jet was almost independent of the superheat of the melt. However, the direction of the jet stream became unstable with increasing superheat of the melt and the fluctuation of the jet diameter at the outlet of the nozzle also increased. The roundness of the cross-section of the obtained fiber increased with decreasing ejection pressure, circumferencial velocity of rotating liquid layer, nozzle diameter, jet incidence angle and density of coolant and with increasing superheat of the melt. The fiber with high roundness could be produced, when the inner pressure of jet was higher than the dynamic pressure of coolant acting on the jet at the incidence point of jet into the liquid layer. The computer simulation of the cooling process of jet has been performed in the temperature range from the ejection to the liquidus temperature of the alloy. The average cooling rates were evaluated to be 0.5∼2.4×105 Ks−1, in the water layer, 1.4∼3.0×104 Ks−1 in the methanol layer and 4.7∼6.5×103 Ks−1 in the salad oil layer, respectively. By using methanol and salad oil as a coolant, a more round fiber could be produced, even if the superheat of the melt was low. The double layers, such as the methanol-water layer and the salad oil-water layer, and the triple layer such as salad oil-methanol-water layers were also effective in producing the fiber with round cross-section.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 60 (4), 420-426, 1996
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681466357248
-
- NII論文ID
- 10001811318
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3954882
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可