- 福田 正
- 東北大学金属材料研究所
書誌事項
- タイトル別名
-
- Effect of Morphology of Grain Boundary Nitride on the Ductility of Fe-30 mass%Cr Alloys
- Fe 30パーセント Cr ゴウキン ノ エンセイ ニ オヨボス リュウカイ チッカブツ ノ ケイタイ ノ エイキョウ
この論文をさがす
抄録
Effects of morphology of grain boundary nitride on the ductility of Fe-30 mass%Cr alloys containing N from 0.004 to 0.13 mass% were investigated. Two kinds of heat treatments were adopted to obtain the morphologies of continuous grain boundary nitride and of discontinuous grain boundary nitride. Tensile tests were carried out at temperatures ranging from 4.2 K to room temperature. Ductility was evaluated by transition temperatures in reduction of area.<BR>The results obtained are summarized as follows:<BR>(1) Upper shelf in reduction of area of the specimen containing discontinuous grain boundary nitride is higher than that of the specimen containing continuous grain boundary nitride.<BR>(2) Transition temperature of the specimen containing discontinuous grain boundary nitride is lower than that of the specimen containing continuous grain boundary nitride.<BR>(3) The area rate of intergranular fracture surface which appears in cleavage fracture surface observed in the specimen containing discontinuous grain boundary nitride is smaller than that which appears in cleavage fracture surface observed in the specimen containing continuous grain boundary nitride. The area rate of intergranular fracture surface which appears in dimple fracture surface also shows similar observation result.<BR>(4) Initiation of microcracks for brittle fracture may be caused by decohesion at the interfaces between the matrix and grain boundary nitride.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 63 (9), 1137-1140, 1999
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467196288
-
- NII論文ID
- 10005345834
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
-
- NDL書誌ID
- 4859051
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可