  • Strengthening of Mg-Al-Ca Die-Cast Alloy with Fine C15-Al<sub>2</sub>Ca Precipitates
  • Mg-Al-Caダイカスト合金における微細C15-Al₂Ca相による析出分散強化
  • Mg-Al-Ca ダイカスト ゴウキン ニ オケル ビサイ C15-Al ₂ Caソウ ニ ヨル セキシュツ ブンサン キョウカ

この論文をさがす

抄録

<p>Age-hardening behavior of a Mg-4.98Al-1.46Ca (mass%) die-cast alloy was investigated at the temperature range between 473 and 623 K. Transmission electron microscopy shows that fine C15-Al2Ca precipitates with a disc-shaped morphology are placed on the (0001) basal plane of the α-Mg matrix phase at the 523 K/10 h peak-aged condition, while they coarsen at the 623 K/100 h over-aged condition. The ultimate tensile strength of the peak-aged alloy is usually higher than that of the over-aged alloy for approximately 40 MPa at both 298 and 473 K, indicating that the precipitation strengthening by fine C15-Al2Ca precipitates is operative even at high temperatures. Dislocations are introduced within the α-Mg matrix phase of the alloy during die-casting; the dislocations are mostly a type and the dislocation segments are mainly located on the (0001) basal plane. The interrelation between fine C15-Al2Ca precipitates and dislocations during tensile deformation is discussed based on the results of tensile tests.</p>

収録刊行物

被引用文献 (9)*注記

もっと見る

参考文献 (31)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ