- Fracture of Leaded Alpha Brass during Hot Working and Improvement of Its Formability
- ナマリ イリ アルファ オウドウ ノ ネツカン カコウ ニ オケル ハカイ キコウ ト ソノ カイゼン
この論文をさがす
抄録
In order to examine the effect of grain boundary sliding on fracture in leaded alpha brass during hot working, hot compression tests with the strain rate of 0.1-0.4 s−1 were carried out at 973 K for Cu-35 mass%Zn including 0-1.5 mass% lead using specimens with three different grain sizes ranging from about 50 to about 200 μm in diameter. In addition, the effectiveness of changing the surface phase for improving poor formability in leaded alpha brass was shown. The results were as follows:<BR>(1) The fracture was influenced by lead content and grain size. In non-leaded alpha brass, fracture did not occur at any grain size. In leaded alpha brass containing 0.5-1.5 mass% lead, the fracture occurred easier with an increase in grain size (>100 μm).<BR>(2) The fracture occureed only at the free surface and was attributed to the grain boundary sliding.<BR>(3) The grain boundary slid more easily as the grain size increased. The amount of sliding was increased by the existence of lead particles. The behavior of grain boundary sliding corresponded to the fracture behavior of leaded alpha brass during hot working.<BR>(4) The poor formability of leaded alpha brass was remarkably improved by changing the phase of the specimen surface from alpha to beta. This result suggests that the alpha grain boundary slides more easily than the beta grain boundary essentially.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 63 (3), 298-304, 1999
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467401856
-
- NII論文ID
- 10002549099
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4691940
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可