放電プラズマ法によって作製したPbTe焼結体の熱電特性に及ぼす結晶粒径の影響

DOI Web Site Web Site 被引用文献1件 参考文献24件

書誌事項

タイトル別名
  • Grain Size Effect on Thermoelectric Properties of PbTe by Spark Plasma Sintering
  • ホウデン プラズマホウ ニ ヨッテ サクセイ シタ PbTe ショウケツタイ ノ ネツデントクセイ ニ オヨボス ケッショウ リュウケイ ノ エイキョウ

この論文をさがす

抄録

Sintered PbTe materials with average grain sizes of 28-309 μm were prepared by spark plasma sintering technique. The apparent densities of the sintered PbTe were 8.17-8.23 Mg/m3, which were higher than 99% of the theoretical one. Thermoelectric properties of the sintered materials and the as-grown boule by Bridgman method were measured in the temperature range from 77 to 350 K. Resistivity, ρ, of the sintered materials increased with decreasing grain size. Temperature dependence of ρ of the sintered PbTe was remarkably different from that of the as-grown boule below 250 K because of potential barriers at grain boundaries. Hall coefficient, RH, of the sintered materials at room temperature increased from 1.4×10−6 to 3.4×10−6 m3/C, as the average grain size increased from 28 to 309 μm, which suggested that oxidation in the crystal grains was caused in the sintering process. Temperature dependence of the thermoelectric power, α, of the sintered PbTe below 250 K reflected the effect of carrier scattering at grain boundaries. Lattice thermal conductivity of the sintered PbTe decreased with decreasing grain size below 250 K, while it was independent of the grain size above that temperature. Above 250 K, thermoelectric properties of the sintered PbTe except those in the 28 μm grain case were consistent with those of the as-grown boule. The values of α and RH at 295 K were calculated by using a two-valence-band model involving a non-parabolic and a parabolic valence band. The calculation results were in good agreement with the experimental data.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 63 (11), 1461-1467, 1999

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (24)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ