- Corrosion of Intermetallic Layer and Reliability of Au/Al Bonds
- Au Al セツゴウブ ニ オケル キンゾク カン カゴウブツソウ ノ フショク キョドウ ト セツゴウ シンライセイ
この論文をさがす
抄録
In order to clarify the reliability on the mechanical and electrical properties of the bond between Au wire and Al thin pad, corrosion behavior of Au-Al intermetallic formed at the bond interface in the molding resin were investigated. The bonds were annealed at several elevated temperatures, T (423-573 K). Typical degradation was recognized by a decrease in bond strength as well as a remarkable increase in electrical resistance. The molding resin has great influence on the corrosion. Bi-phenyl (BP) epoxy resin was found to cause the degradation approximately six times faster than o-cresole novolac (OCN) epoxy. Activation energies of the bond failure were 1.5 eV (T>450 K) and 2.0 eV (T<450 K) in BP resin and 2.3 eV in OCN resin.<BR>The corroded part was revealed to be Au4Al intermetallic phase formed in the bond interface. The growth rate of corroded layer was proportional to annealing time t, which indicated the corrosion behavior was not diffusion-controlled. Activation energies of the growth rate of corroded layer in the BP and the OCN resin were 1.6 eV, 2.3 eV, respectively, which were very similar to those of the bond failure.<BR>The corrosion reaction of Au4Al and bromide produced minute Au precipitation (fcc) and Al oxide formation. The Al oxide was identified to be amorphous by EDS and electron diffraction.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 63 (3), 406-415, 1999
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467474304
-
- NII論文ID
- 130007341416
- 10002549415
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4692399
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可