Studies on Impact Fatigue : part II, Inelastic Behavior of S50C Steel under Impact Fatigue Loads
この論文をさがす
説明
Using plain specimens of annealed S50C carbon steel, fatigue tests were conducted under fully reversed sinusoidal axial stress and under repeated impact stress. Inelastic behavior of specimens was observed using strain gauges mounted on the specimens. Under the impact fatigue stress, fractures occurred at the stress levels lower than the ordinary fatigue limit and in the region of a larger number of stress cycles than 107. The inelastic strains accompanied with a fracture were unexpectedly small comparing with those under sinusoidal stress. And the amount of hysteresis energy accumulated : in the specimen during the impact fatigue test was also less than the corresponding value under sinusoidal stress.
収録刊行物
-
- Bulletin of JSME
-
Bulletin of JSME 17 (113), 1379-1388, 1974
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467566208
-
- NII論文ID
- 110002360410
-
- NII書誌ID
- AA0058509X
-
- ISSN
- 18811426
- 00213764
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可