- Nodular Corrosion of Zirconium Alloys and XPS Analysis of Surface Oxide Layer
- ジルコニウム ゴウキン ノ ノジュラー フショク ト ソノ ヒョウメン サンカ
この論文をさがす
説明
Nodular corrosion takes place in cladding tubes of the boiling water reactor. In order to understand the mechanism of the nodular corrosion, a series of corrosion tests was performed with pure Zr and Zr-M binary alloys (M=Sn, Fe, Cr, Ni) by exposing them to the steam environment of 773 K and 10.3 MPa. The chemical composition of the oxide layer formed on the specimen surface was analyzed using X-ray photoelectron spectroscopy. As a result, it was found that the distribution of alloying elements, M, in the oxide layer was relatively uniform in the case of uniform corrosion, whereas it was very non-uniform in the case of nodular corrosion. For example, in the latter case, alloying elements such as Cr and Sn were condensed mainly in the outer surface of the oxide layer. Such a non-uniform distribution of alloying elements will not be arisen from the heterogeneous distribution of alloying elements in the mother alloy, but will be introduced to the oxide layer on the alloy in the course of corrosion. The segregation of alloying elements will disturb the uniform growth of the oxide layer, resulting in the onset of nodular corrosion on the surface.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 62 (6), 534-541, 1998
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467773824
-
- NII論文ID
- 10007632990
- 130007341660
- 10001970032
-
- NII書誌ID
- AN00062446
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4512259
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可