Thermodynamic Investigation on Molten Cu-Ni-Fe Alloys by the Double Knudsen Cell-Mass Spectrometer System
-
- Fujita Yasuyo
- Institute for Advanced Materials Processing, Tohoku University
-
- Pagador Romeo U.
- Institute for Advanced Materials Processing, Tohoku University
-
- Hino Mitsuhisa
- Institute for Advanced Materials Processing, Tohoku University
-
- Azakami Takeshi
- Department of Mechanical Engineering, Saitama Institute of Technology
Bibliographic Information
- Other Title
-
- クヌーセンセル-質量分析法による溶融Cu-Ni-Fe系合金の熱力学的研究
- クヌーセンセル シツリョウ ブンセキホウ ニヨル ヨウユウ Cu Ni Feケ
Search this article
Abstract
For thermochemical analysis of the phase equilibrium between the nickel alloy and slag phases in relation to the nickel smelting process, the mass spectrometer combined with a double Knudsen cell was adopted to measure the activities of the elements in the molten Cu-Ni and Cu-Ni-Fe alloys and the activity of sulfur below 5 at%S in the ternary alloys at 1623 K. A major feature of this set-up is that the activity values of the components can be determined at every experimental point without applying the Belton-Fruehan equation which requires the ion intensity measurement over the whole alloy composition region. In the present study, the following results were obtained.<BR>(1) The activities of copper and nickel in the molten Cu-Ni alloys show a slightly positive deviation from the Raoult’s law and the activity behavior is consistent with a reference in the composition region higher than 50 at%Cu.<BR>(2) The copper activity in the composition region over 30 at%Cu of the Cu-Ni-Fe ternary system shows a positive deviation from the ideal behavior and the deviation increases with increasing iron content in the Cu-Ni alloy.<BR>(3) The activity coefficients of sulfur at infinite dilute solution in the Cu-Ni-Fe ternary alloys are found to be between 3 to 4×10−2 in the composition region over 30 at%Cu. This tendency agrees with the sulfur behavior expected from the Cu-Ni-S and Fe-Ni-S systems.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 61 (7), 619-624, 1997
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681468517760
-
- NII Article ID
- 10001966926
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 4267892
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed