- 日比野 敦
- 電気通信大学電気通信学部機械制御工学科
書誌事項
- タイトル別名
-
- Analysis of Combustion Synthesis Process of TiAl Intermetallic Compound by Dipping Experiment of Ti Wire into Al Melt
- ヨウユウ Al エ ノ Tiセン シンセキ ジッケン ニヨル TiAl キンゾ
この論文をさがす
説明
The combustion synthesis process has attracted attention as new synthesizing technology of intermetallic compounds. However, as the products tend to be porous and the process control condition is not clear, the process has not been put in practical use. To realize the production of intermetallic compounds by combustion synthesis process, fundamental mechanism or compound formation stages in the combustion reaction should be made clear. In this paper, the compound formation behavior between the Ti and the Al melt was measured, and the compound formation stages in the combustion synthesis of TiAl was investigated.<BR>Dipping experiment which dipped a Ti wire into the Al melt was performed under various conditions of the holding time and temperature. On the other hand, the Ti/Al mixed compacts were quenched during the thermal explosion reaction. The compound formation stage of TiAl was estimated by comparison between the cross section of dipped wires and the microstructure of quenched compacts.<BR>By the dipping experiment, it was found that the compound formation behavior in the Ti-Al system changed with temperature. At the low temperature such as 973∼1173 K, the formation reaction of TiAl3 took place, and small dispersive particles were formed around a Ti wire. However, in the dipping at high temperature as 1373 K or 1473 K, the Ti(α, β) solid solution formed in the wire. In a quenched compact, these phases were detected as well. The TiAl3 phase was found in a compact quenched at the initial stage of synthesis, and the Ti(α, β) solid solution phase was observed at the middle stage. Therefore, it was estimated that the compound formation in the TiAl combustion synthesis progressed through the formation of these phases. As the synthesis reaction was affected by the combustion temperature, the temperature control is of importance to improve the microstructure and synthesized phase of the product.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 61 (2), 128-134, 1997
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681468936704
-
- NII論文ID
- 10001965732
- 10005139479
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
-
- NDL書誌ID
- 4139988
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可