Fatigue Fracture Behavior of High-Strength Steel in Super Long Life Range.
-
- MURAKAMI Ri-ichi
- Department of Mechanical Engineering, The University of Tokushima
-
- YONEKURA Daisuke
- Department of Mechanical Engineering, The University of Tokushima
-
- NI Zhengdong
- Graduate Student, The University of Tokushima
この論文をさがす
説明
Long term cantilever-type rotational bending fatigue tests of up to 109 cycles were carried out on high carbon chromium bearing steel, SUJ2. The fatigue fracture behavior of SUJ2 in the super long life range was discussed based on scanning electron microscope observations and fracture mechanics. Fatigue failure occurred when the number of cycles exceeded 107. In the super long life range, the fish-eye-type fracture and the subsurface-type fracture were observed. In the fish-eye-type fracture, the stress intensity factor calculated from the area of the facet region was independent of the number of cycles to failure and was almost constant at 5.4MPa• m1/2. In the subsurface-type fracture, high carbon segregation was observed at the crack initiation area. The stress intensity factor for the carbon segregation area was close to 5.0MPam1/2. Pure fatigue crack was initiated from the area outside the facet region or the high carbon segregation area.
収録刊行物
-
- JSME International Journal Series A Solid Mechanics and Material Engineering
-
JSME International Journal Series A Solid Mechanics and Material Engineering 45 (4), 517-522, 2002
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681469614848
-
- NII論文ID
- 10016190658
-
- NII書誌ID
- AA11179396
-
- COI
- 1:CAS:528:DC%2BD3sXps1ak
-
- ISSN
- 13475363
- 13447912
-
- NDL書誌ID
- 6329963
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可