Thermal Crack in the Carbide Face-Milling Cutter : 2nd Report, Its Significance as a Cause of Tool Failures
Bibliographic Information
- Other Title
-
- Thermal crack in the carbide face-milling cutter,2
Search this article
Description
Several types of cracks which appear in the carbide face-milling cutter, including the thermal crack, are investigated in respect with their signiflcances as the causes of tool failures which occur over a wide range of the cutting speeds. Tool failures at high cutting speeds are classified into several types from their appearances and each type concerns a singular crack. The so-called thermal crack is one of these cracks which cause the tool failures at high cutting speeds. The cutting speed, the feed and the cutting fluid influence the type of the crack which causes the tool failure so that the type of the failure changes. Including the thermal crack, some cracks are explainable as being due to the fatigue of the carbide at an elevated temperature. But there are a few of cracks that do not conform to the above mentioned explanation.
Journal
-
- Bulletin of JSME
-
Bulletin of JSME 6 (22), 317-326, 1963
The Japan Society of Mechanical Engineers
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681469710080
-
- NII Article ID
- 110002360976
-
- NII Book ID
- AA0058509X
-
- ISSN
- 18811426
- 00213764
-
- NDL BIB ID
- 9247558
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL Search
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed