- DOHDA Kuniaki
- Department of Mechanical Engineering, Gifu University
-
- KUBOTA Hiroyuki
- Doctoral Student, Gifu University
-
- TSUCHIYA Yoshinari
- Metallic Material Lab., Toyota Central R&D Labs., Inc.
この論文をさがす
説明
The possibilities of application of DLC-Si coating to the die in dry ironing process have been investigated by strip-ironing type tribometer. Alloy tool steel and high speed steel were used as substrate material for ironing dies. Two types of substrate surface texture were prepared by lapping and grinding. And two types of die edge angle were prepared. High tensile strength steel and brass were tested as workpieces. The surface appearance of die, friction coefficient during ironing and surface roughness of ironed workpiece were measured. The friction coefficient of DLC-Si coated die in the dry ironing process is relatively low. Galling does not occur on the die surface. In case of high tensile strength steel, the damage grows with the number of tests. The surface roughness of a brass workpiece does not increase with repeat ironing. The DLC-Si coating could be applied to the dry ironing process in this investigated condition.
収録刊行物
-
- JSME International Journal Series A Solid Mechanics and Material Engineering
-
JSME International Journal Series A Solid Mechanics and Material Engineering 48 (4), 286-291, 2005
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681471329152
-
- NII論文ID
- 110004820571
-
- NII書誌ID
- AA11179396
-
- COI
- 1:CAS:528:DC%2BD2MXhtlCisbfL
-
- ISSN
- 13475363
- 13447912
-
- NDL書誌ID
- 7473465
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可