Anode Properties of Cu-Coated Si Thick Film Electrodes Prepared by Electroless Deposition and Gas-Deposition
-
- USUI Hiroyuki
- Department of Chemistry and Biotechnology, Graduate School of Engineering, Tottori University
-
- NISHINAMI Hiroyuki
- Department of Chemistry and Biotechnology, Graduate School of Engineering, Tottori University
-
- IIDA Takahisa
- Department of Chemistry and Biotechnology, Graduate School of Engineering, Tottori University
-
- SAKAGUCHI Hiroki
- Department of Chemistry and Biotechnology, Graduate School of Engineering, Tottori University
この論文をさがす
抄録
Thick film electrodes of Cu-coated Si particles were fabricated by an electroless deposition and a successive gas-deposition, and were evaluated their electrochemical properties as an anode of Li-ion battery. The discharge capacity and its retention at the 1000th cycle were 570 mAh g−1 and 61%. The excellent cycle life performance is attributed to an enhanced electrical conductivity due to the Cu-coating and a reversible conversion reaction between Li and Cu2O which was formed on the Cu surface. The high capacity retention is caused by a high fracture toughness of the coated Cu which can effectively relax a stress induced by volume expansion of Si as a buffer matrix.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 78 (5), 329-331, 2010
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681472500864
-
- NII論文ID
- 10026165539
-
- NII書誌ID
- AN00151637
-
- COI
- 1:CAS:528:DC%2BC3cXlvFymsL4%3D
-
- ISSN
- 21862451
- 13443542
- http://id.crossref.org/issn/13443542
-
- NDL書誌ID
- 10662528
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可