Post-annealing Effects on Reaction Selectivity of Methanol Oxidation at Carbon-based Platinum Co-sputtered Electrocatalyst
-
- INOUE Mitsuhiro
- Hydrogen Isotope Research Center, University of Toyama
-
- NAGAI Kazuhiro
- Department of Materials Science and Technology, Faculty of Engineering, Nagaoka University of Technology
-
- SHIRONITA Sayoko
- Department of Materials Science and Technology, Faculty of Engineering, Nagaoka University of Technology
-
- ABE Takayuki
- Hydrogen Isotope Research Center, University of Toyama
-
- UMEDA Minoru
- Department of Materials Science and Technology, Faculty of Engineering, Nagaoka University of Technology
この論文をさがす
抄録
A carbon with Pt (C–Pt) catalyst was prepared by a co-sputtering technique. Pt4f peaks of the prepared sample were observed at higher binding energies than those of a Pt sputtered sample. These Pt4f peaks shifted to the low binding energies with an increase in a post-annealing temperature, whereas the C1s peak position was unchanged. For the C–Pt catalyst as sputter-deposited, the methanol oxidation performance was enhanced by the presence of O2. This O2-enhnaced methanol oxidation was suppressed by the post-annealing at 160°C, while the reaction selectivity of the methanol oxidation was retained.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 83 (5), 368-371, 2015
公益社団法人 電気化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681474932608
-
- NII論文ID
- 130005067096
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 026362327
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用可