- Degradation Mechanisms of Electric Double Layer Capacitors with Activated Carbon Electrodes on High Voltage Exposure
- カッセイタン デンキョク オ モチイタ デンキ ニジュウソウ キャパシタ ノ コウデンアツ サドウ カ ニ オケル レッカ キコウ
この論文をさがす
抄録
Degradation mechanism of electrochemical double layer capacitors on high-voltage exposure is examined. Capacitance loss for positive electrodes is significantly accelerated above 4.5 V (vs. Li/Li+) whereas that of negative electrodes occurs on the electrochemical cycles down to 1.2 V. The surface of positive electrodes is covered with decomposition products of propylene carbonate used as electrolyte solution, and therefore high-voltage exposure increases impedance of electrodes. In contrast, the degradation of negative electrodes is triggered by the decomposition reaction of electrolyte salts, resulting in the formation of radical species. It is proposed that the radical species attack fluorinated polymer used as a binder, leading to the defluorination of binders and thus increase in polarization on electrochemical cycles.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 83 (8), 609-618, 2015
公益社団法人 電気化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681475337600
-
- NII論文ID
- 130005091990
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 026629916
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可