低炭素鋼板の延性に及ぼす固溶炭素および<br>セメンタイトの影響

DOI Web Site 被引用文献2件 参考文献14件

書誌事項

タイトル別名
  • Effects of Carbon in Solid Solution and Cementite Density on Ductility of<br>Low-Carbon Al-Killed Steel Sheet
  • テイタンソ コウハン ノ エンセイ ニ オヨボス コヨウ タンソ オヨビ セメンタイト ノ エイキョウ

この論文をさがす

抄録

A systematic study on the effects of solute carbon and cementite density on ductility was conducted in low-carbon Al-killed steel with 0.022 mass% C. The results obtained are as follows; 1) Total elongation was impaired by the presence of solute carbon. The deterioration is mainly caused by a decrease in local elongation; however, uniform elongation is hardly affected by solute carbon. The dynamic strain aging due to solute carbon is considered to impair local elongation, because necking is promoted by local softening when strain rate increases locally. 2) Total elongation is impaired by the presence of intragranular cementites, but is hardly affected by grain boundary cementites. Uniform elongation decreases clearly with increasing density of intragranular cementites, which is caused by a significant increase in yield strength. Furthermore, since intragranular cementites form voids, they may impair local elongation due to ductile fracture. However, when their density becomes high, in other words, they become significantly small, a slight improvement in local elongation is observed. Grain boundary cementites have no effects on the tensile properties of low-carbon Al-killed steel within the scope of the present study.

収録刊行物

  • 塑性と加工

    塑性と加工 51 (594), 690-694, 2010

    一般社団法人 日本塑性加工学会

被引用文献 (2)*注記

もっと見る

参考文献 (14)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ