Tensile Characteristics of High-Cr-Fraction Cr-Cu Composite at Various Temperatures
-
- TERAO Hoshiaki
- JFE精密株式会社
-
- MATSUMOTO Yoshihisa
- 大分工業高等専門学校,機械工学科
-
- KANETAKE Naoyuki
- 名古屋大学,大学院工学研究科
Bibliographic Information
- Other Title
-
- 高配合率Cr-Cu複合材の引張特性における温度依存性
- コウハイゴウリツ Cr-Cu フクゴウザイ ノ ヒッパリ トクセイ ニ オケル オンド イソンセイ
Search this article
Abstract
In order to gain the fundamental knowledge of plastic deformability in a Cr-Cu composite material containing a high fraction of Cr particles, tensile tests of 50mass%Cr-Cu composites were performed at 299K to 473K. Although single-phase Cr generally shows brittle fracture at temperatures lower than approximately 350K, the Cr-Cu composite shows ductile fracture at all tested temperatures. The tensile strength and fracture elongation decreased with increasing testing temperature. These tensile properties of the high-Cr-fraction Cr-Cu composite originate from the properties of a matrix material comprising a Cu alloy with a small amount of dissolved and precipitated Cr. However, the reduction in area was increased with increasing testing temperature. The deformation characteristics of the Cr-Cu composites were considered in terms of the re-arrangement, elongation, and rotation of Cr particles in a ductile Cu matrix. In addition, the ductile-brittle transition behavior of Cr particles would affect the tensile property of Cr-Cu composite at 353K to 373K, which is the range of the ductile-brittle transition temperature (DBTT).
Journal
-
- Journal of the Japan Society for Technology of Plasticity
-
Journal of the Japan Society for Technology of Plasticity 56 (648), 34-39, 2015
The Japan Society for Technology of Plasticity
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681476344192
-
- NII Article ID
- 130004787568
-
- NII Book ID
- AN00135062
-
- ISSN
- 18820166
- 00381586
-
- NDL BIB ID
- 026051164
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed