Zn-Al₂O₃ Composites with High Aluminum Content and Nanostructured Al₂O₃/ZnO Prepared by Electrochemical Technique from Non-Suspended Solution
-
- ARAKAWA Tomiyuki
- Institute of Science and Technology, Kanto Gakuin University
-
- WATANABE Nobuaki
- College of Science and Engineering, Kanto Gakuin University
-
- CHOKKI Kenta
- College of Science and Engineering, Kanto Gakuin University
-
- YABE Kazuhiro
- Oki Engineering Co., Ltd.
-
- KOIWA Ichiro
- College of Science and Engineering, Kanto Gakuin University Graduate School of Engineering, Kanto Gakuin University
書誌事項
- タイトル別名
-
- Zn-Al<sub>2</sub>O<sub>3</sub> Composites with High Aluminum Content and Nanostructured Al<sub>2</sub>O<sub>3</sub>/ZnO Prepared by Electrochemical Technique from Non-Suspended Solution
この論文をさがす
抄録
Zn-Al2O3 composites were electrodeposited from a non-suspended solution containing ZnSO4·7H2O and Al2(SO4)3·14–18H2O using benzyldimethyltetradecylammonium chloride dehydrate (BDTAC) as the additive at an electrodeposition current of 50–500 A/m2 with an air or a nitrogen bubbling. Initial layers with a thickness of approximately 1 µm were observed in the Zn-Al2O3 composite on copper substrates. Furthermore, the Zn-Al2O3 composite was composed of two different crystallographic areas, namely, nano-level size deposited grains with 20–60 nm in width and 100–200 nm in length, and closely packed fine particle deposits with a diameter of approximately 5 nm containing more than 26 atomic% aluminum. The nano-level size deposited grains and the closely packed fine particle deposits comprised nano-size ZnO and θ-Al2O3, respectively. The oxygen concentration in Zn-Al2O3 composite by the air bubbling was higher than that in Zn-Al2O3 composite by the nitrogen bubbling. In contrast, the zinc content ratio in Zn-Al2O3 composite by the air bubbling was lower than that in Zn-Al2O3 composite by the nitrogen bubbling. The aluminum concentration in closely packed fine particle deposits in Zn-Al2O3 composite by the air bubbling was almost the same value as that in Zn-Al2O3 composite by the nitrogen bubbling.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 85 (6), 315-318, 2017
公益社団法人 電気化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681476644736
-
- NII論文ID
- 130007342832
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 028212296
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可