- High Temperature Oxidation of High Chromium White Cast Iron
- コウクロム ハク チュウテツ ノ コウオン サンカ
この論文をさがす
抄録
Atmospheric high temperature oxidation behavior was studied on high chromium cast iron containing 2.2 to 4.1 % C and 19 to 26 % Cr at 953 to 1223 K. Though the Cr content of the matrix in 25 % chromium cast iron was fairly lower than that of stainless steel, the former exhibited a better oxidation resistance than the latter. Cr rich primary and eutectic M7C3, and also secondary carbide suppressed the progress of the oxidation of matrix. 25 % Cr eutectic specimens, composed of fine (matrix + M7C3) eutectic structures, showed the highest oxidation resistance. A protective continuous oxide layer of Cr2O3 was formed on the 25 % Cr specimens, while the oxide layer on the 20 % Cr specimens consisted mostly of Fe2O3.
収録刊行物
-
- 鋳造工学
-
鋳造工学 73 (1), 3-8, 2001
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681482654208
-
- NII論文ID
- 10005743818
- 10007814912
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 5643693
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可