Surface Hardening of Cast Iron Inserted WC Particles
-
- Aso Setsuo
- Faculty of Engineering and Resource Science, Akita University
-
- Nakanishi Makoto
- Graduate Student, Akita University
-
- Goto Shoji
- Faculty of Engineering and Resource Science, Akita University
-
- Ike Hiroyuki
- Iwate Industrial Research Institute
-
- Shobuzawa Yoshiyuki
- Iwate Industrial Research Institute
Bibliographic Information
- Other Title
-
- WC粉末による鋳鉄の表面硬化
- WC フンマツ ニ ヨル チュウテツ ノ ヒョウメン コウカ
Search this article
Abstract
WC particles were inserted near the surface of gray irons. Particles of three different sizes were inserted individually or mixed with the particles of other alloy elements, The inserted layer was observed from the vertical section with an EPMA. It was confirmed that an inserted layer of about 4 mm thick can be formed without any defects near the surface of gray irons. The base metal of the inserted layer was usually the same as the mother gray iron. However, the Cr or Mo alloying favored the formation of white cast irons. Microstructures of the layer inserting coarse WC particles were different from that of the fine WC particles. The coarse WC particles were bridged by the γ + M3C eutectic layers, however, fine WC particles dispersed uniformly in both eutectic phases. The hardness of the mother gray irons ranged from Hv120 to 200 while the hardness of the Cr alloying inserted layer increased more than Hv700.
Journal
-
- Journal of Japan Foundry Engineering Society
-
Journal of Japan Foundry Engineering Society 73 (3), 155-160, 2001
Japan Foundry Engineering Society
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681483192704
-
- NII Article ID
- 130004556374
- 10007483746
-
- NII Book ID
- AN10514770
-
- COI
- 1:CAS:528:DC%2BD3MXjtVGitL8%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL BIB ID
- 5706765
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
- Crossref
-
- Abstract License Flag
- Disallowed