鋳型を考慮した弾塑性応力解析による球状黒鉛鋳鉄鋳物のひけ巣予測

DOI Web Site 被引用文献2件

書誌事項

タイトル別名
  • Prediction of Porosity Defects in Spheroidal Graphite Iron Castings by Elasto-plastic Stress Analysis Including Mold
  • イガタ オ コウリョ シタ ダン ソセイ オウリョク カイセキ ニ ヨル キュウジョウ コクエン チュウテツ イモノ ノ ヒケ ス ヨソク

この論文をさがす

説明

  A method for predicting porosity defects in spheroidal graphite (SG) iron castings with sand mold using critical stress values specific to melt was studied by comparing experimental results with stress distribution obtained by numerical stress analyses including mold strength effects. The elastic perfectly plastic volume pixel finite element method (VOXEL-FEM) was introduced to calculate stress distribution of the castings. The analysis considered elastic deformation of mold and contacts between the mold and casting. Young's modulus of the mold was estimated from the relation between mold elasticity and strength. Porosity volume in the calculation was defined as the volume of element where average stress exceeds the critical stress. As a result of comparing the calculated results with porosity observations under various mold strengths, the critical stress was estimated to be about 3.5 MPa, confirming that defective regions can be quantitatively predicted with this critical stress. Furthermore, the proposed method was applied to a casting with green sand mold. The calculated results showed that green sand mold has little influence on stress distribution and porosity volume of the casting as shown by experimental results.

収録刊行物

  • 鋳造工学

    鋳造工学 77 (9), 622-628, 2005

    公益社団法人 日本鋳造工学会

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ