減圧処理による片状黒鉛鋳鉄の組織に及ぼす酸素の影響

DOI Web Site

書誌事項

タイトル別名
  • Effects of Oxygen for Structure of Gray Cast Iron by Vacuum Depressurization Processing
  • ゲンアツ ショリ ニ ヨル ヘンジョウ コクエン チュウテツ ノ ソシキ ニ オヨボス サンソ ノ エイキョウ

この論文をさがす

説明

  In order to clarify the effects of oxygen on graphitization in cast iron, various pig irons were melted in air and held for various duration under vacuum ranging from 1 Torr to 5 Torr at 1773 K to 1823 K. Molten iron was cast into green sand mould in air, and round bar specimens were made. Fractures and microstructures of round bar affected by oxygen were studied.<br>  The total oxygen and that dissolved in molten iron were measured. In the first stage of the decompression process, the dissolved oxygen content had a tendency to increase slightly, and decreased as low as 2 massppm afterwards. As the processing time increases, the flake graphite structure changed from type A (or type D plus chill structure) to an increase in the chill structure to inverse chill, and finally to the type D graphite structure (without chill). The molten iron of D which was held for 30 minutes under low pressure was added with 3% Fe-Si-Ca for inoculation. The graphite in irons spheroidized easily.

収録刊行物

  • 鋳造工学

    鋳造工学 77 (9), 608-614, 2005

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ