- Effect of Copper on Ferritization of Spheroidal Graphite Cast Iron
- キュウジョウ コクエン チュウテツ ノ フェライトカ ニ オヨボス ドウ ノ
この論文をさがす
説明
Ferritization of spheroidal graphite cast iron (SGI) containing tin or copper has been investigated. The SGIs of different contents of copper or tin were isothermally held for various lengths of time below the eutectoid temperature after austenitizing. Tin in SGI promotes pearlite formation and retards ferrite formation, while copper in SGI retards both ferrite and pearlite formation. The onset of ferrite formation is markedly retarded in SGIs containing 1% Cu or above accompanied by an incubation period of transformation. Furthermore, growth rate of ferrite decreases with increasing copper content. Retardation of ferrite growth is brought about by the onset of pearlite formation. The growth rate of pearlite is markedly higher than that of ferrite, except at specific temperature range. It is found that ferrite formation tends to be retarded in the inner part of large SGI blocks containing 0.5 % Cu.
収録刊行物
-
- 鋳造工学
-
鋳造工学 70 (3), 169-174, 1998
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681483537408
-
- NII論文ID
- 10002553552
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 4437161
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可