- Effects of Sulfur and Silicon on Inter-Graphite Spacing in Unidirectionally Solidified Fe-C Alloy
- 1ホウコウ ギョウコシタ Fe Cケイ ゴウキン ノ コクエンヘン カンカク
この論文をさがす
抄録
The effects of sulfur and silicon on inter-graphite spacing λ in gray cast iron has been investigated by unidirectional solidification with Bridgman method. Sulfur content was varied from 0.004 to 0.108mass%, and silicon content was varied from 0.068 to 1.10mass%. The speed of crucible V was varied from 0.00015 to 0.01000cm/s. The temperature gradient at solid-liquid interface was 18∼21K/cm. The experimental equations of λ-V were obtained by using linear regression analysis. It was clarified that the transition from flake to undercooled graphite shifted differently according to sulfur and silicon content.
収録刊行物
-
- 鋳造工学
-
鋳造工学 69 (4), 297-303, 1997
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681483652608
-
- NII論文ID
- 10003800126
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 4194330
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可