渦電流試験による鋳鉄表面近傍におけるきずの検出

書誌事項

タイトル別名
  • Flaw Detection in Near Surface of Cast Iron by Eddy Current Testing
  • ウズデンリュウ シケン ニ ヨル チュウテツ ヒョウメン キンボウ ニ オケル キズ ノ ケンシュツ

この論文をさがす

抄録

  Eddy Current Testing (ECT) was applied to non-destructive evaluation of artificial cracks, 0.25 mm in width made by electro discharge method, and internal defect, 1.6 mm diameter drill hole under the surface, in cast iron. It is important to select suitable frequency and coil for measurement to receive higher SIN signal, because small skin depth caused by ferromagnetism of a matrix limits measurable depth and inhomogeneous structure produces strong noise signal. Measurable crack depth was less than 3 mm when using two coil method. Direction of the crack could be determined from Lissajous patterns of the ECT signal. The signal changed linearly when two coils set in right angle to the crack, but showed curve when two coils set parallel with the crack. On the other hand, detection of internal defect of cast iron was difficult because change in Lissajous patterns of the ECT signal by a drill hole under 0.5 mm from the ground surface was weak as compared to higher noise signal induced by inhomogeneous matrix.

収録刊行物

  • 鋳造工学

    鋳造工学 77 (12), 821-825, 2005

    公益社団法人 日本鋳造工学会

参考文献 (6)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報

問題の指摘

ページトップへ