- Analysis of Quenching Crack Generation in Low Alloy Cast Steel by Using Heat Treatment Simulation
- ネツ ショリ シミュレーション オ カツヨウ シタ テイゴウキン チュウコウザイ ノ ヤキワレ ハッセイ ノ カイセキ
この論文をさがす
説明
In order to clarify the quenching crack phenomenon in cast steel, a disk shaped low alloy cast steel specimen with an opening was quenched in water at 1123 K. The generation of quench crack was studied by microstructure observation and analyzed by heat treatment simulation. The results obtained were as follows. (1) Quenching cracks form easily as the specimen volume increases. Quenching cracks occur due to time lag in martensitic transformation at the surface side and inner side of the quenched specimen. (2) Minute quenching cracks occur first at the boundary, alter which each microcrack joined together and grew into a maincrack. (3) Moreover, the quenching crack showed a very sharp grain boundary fracture, and since the grain boundary strength was lower than that in transgranular, quenching cracks of low alloy steel casting materials are considered due to martensitic transformation stress in that mid and high temperature regions. (4) Heat treatment simulation showed quenching occurs at maximum principal stress concentration positions. The stress concentration location and quenching crack position are influenced by specimen shape. (5) Quenching crack generation was demonstrated by the heat treatment simulation, clarifying that the crack is generated not by heat stress but by martensite transformation stress.
収録刊行物
-
- 鋳造工学
-
鋳造工学 77 (7), 437-444, 2005
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681484327168
-
- NII論文ID
- 10016590087
-
- NII書誌ID
- AN10514770
-
- COI
- 1:CAS:528:DC%2BD2MXps1Cgtrk%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 7422906
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可