- タイトル別名
-
- Microstructure and Its Stability of Semi-Solid Fe-C Slurry by Powder Compaction
- アップンタイ カネツホウ ニヨル テツ タンソケイ コエキ キョウゾン スラリ
この論文をさがす
説明
An investigation was carried out to clarify the microstructures of semi-solid Fe-C alloys made by the powder compaction of pure iron powders and cast iron powders with eutectic composition. In the rapid heating of mixed compact, the probability of the collisions of solids was much lower than that in the stirring method. The size of the solid particles was therefore expected to be much smaller than that in the stirring method. The shape of the solid particles was spheroidal as those acquired by the stirring method. The average size of the solid particles was 50 μm on the polished surface. The solid particles, which were former by pure iron, had martensite structure. The microstructure of matrix was fine ledeburite. It was found that the slurry made by the method had fine microstructure and stability of fine solid particles against isothermal holding ideal for thixocasting.
収録刊行物
-
- 鋳物
-
鋳物 67 (7), 465-470, 1995
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681484393600
-
- NII論文ID
- 10001750642
-
- NII書誌ID
- AN00016813
-
- COI
- 1:CAS:528:DyaK2MXos1ahu78%3D
-
- ISSN
- 21860335
- 00214396
-
- NDL書誌ID
- 3629177
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可