- Fractal Analysis of Porosity Area Distribution in Die Casting Using X-ray CT Image
- Xセン CT ガゾウ オ モチイタ ダイ カストナイ イス メンセキ ブンプ ニ タイスル フラクタル カイセキ
この論文をさがす
説明
Pores in pressure die castings are generated by entrapped gases or solidification shrinkage. To determine the pore formation mechanism and prevent the formation of pores, the morphology of pores, such as their shape and spatial distribution, should be quantitatively evaluated, and the cause of pores, such as gas or shrinkage, must be quantitatively specified. The accurate identification of pores requires a huge amount of knowledge about the die casting process, the lack of which may lead to misjudgment. We previously introduced a fractal dimension to quantitatively identify the cause of pores and verified the validity of using the fractal dimension DaM, calculated by the spatial distribution of the areas of pores from optical micrograph images. This fractal dimension can also be calculated from an X-ray CT image, which allows nondestructive inspection. However, X-ray CT images generally have lower resolution than optical micrographs. In this study, we examined the validity of identifying the cause of pore formation using the fractal dimension DaX, calculated from X-ray CT images, by comparison with DaM. In aluminum alloy die castings, DaX was found to have a lower value inside the samples than on the surface. This result showed that the effect of shrinkage increases in the inner area, which is consistent with the behavior of DaM Therefore, the evaluation of DaX is also expected to provide sufficient information to identify the cause of pore formation.
収録刊行物
-
- 鋳造工学
-
鋳造工学 80 (5), 284-289, 2008
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681484880896
-
- NII論文ID
- 10021162130
-
- NII書誌ID
- AN10514770
-
- COI
- 1:CAS:528:DC%2BD1cXnt1yltL8%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 9512275
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可