- Improvement of Frictional Wear Property of Lead-free Bronze Castings by Lamellar Eutectoid Structure
- ソウジョウ キョウセキ ソシキ ニ ヨル ナマリ フリー セイドウ イモノ ノ マサツ マモウ トクセイ ノ コウジョウ
この論文をさがす
説明
As the substitute of lead bronze, a metallic structure control technique applying eutectoid transformation was employed to develop lead-free or low lead copper alloys for bearings. Considerable lamellar eutectoid structures made of copper-tin based intermetallic compound and copper solid solution containing fine bismuth precipitates were dispersed in as-cast alloys by means of an alloy design technique. The lamellar eutectoid structure was formed between primary α dendrite arms after transformation of a part of β phase without producing granular δ phases. In the range of tin content from 4 to 12mass%, the amount of the eutectoid structure was linearly increased with the tin content. Above 12mass%, the amount of the eutectoid was decreased with increasing tin content. Alloys containing the lamellar eutectoid structure showed higher anti-seizing and higher abrasion resistances than those of the lead bronze LBC3, suggesting that the formation of the laminate composite structure and precipitation of fine bismuth particles produce excellent wear-resistance.
収録刊行物
-
- 鋳造工学
-
鋳造工学 83 (9), 513-518, 2011
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681487497856
-
- NII論文ID
- 10029579874
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 11233087
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可