- Studies on Hardening of Amino Resins
- I.“Formaldehyde Isolation Test” as the Method for Determining the Degree of Cure of Melamine-Formaldehyde Resin
- 第1報メラミン樹脂の硬化度測定法としての“ホルムアルデヒド溶出試験法”
抄録
A method for determining the degree of cure of melamine-formaldehyde resin and factors influencing the test were studied on laminate.<BR>A test piece (30-50mm) was dipped into 50ml of water or dilute sulphuric acid at various temperatures (60-100°C) and times (3-80min).<BR>Formaldehyde and melamine were dissolved in the solution due to the dissociation of methylol and the decomposition of methylene groups.<BR>Formaldehyde dissolved into 0.95-3.03% sulphuric acid at 100°C for 10min was almost attributed to the remaining methylol groups in hardened resin, therefore, the amount of formaldehyde indicated the relative degree of cure of resin.<BR>Among the factors on “formaldehyde isolation test”, curing temperature was more effective than curing time, and pressure was no effect.<BR>The activation energies of the dissociation of methylol and the decomposition of methylene groups were ca. 20 and 29kcal/mol, respectively.
収録刊行物
-
- 高分子化學
-
高分子化學 21 (233), 529-538, 1964
公益社団法人 高分子学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681496381440
-
- NII論文ID
- 130004032473
-
- ISSN
- 18848079
- 00232556
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可