- Molecular Structure of High Pressure Polyethylene
- VI. Expansion Factors of Some Commercial High Pressure Polyethylenes and Consideration on MI- [η] Correlation
- 第6報 市販高圧法ポリエチレンのexpansion factorとMI- [η] の関係
この論文をさがす
説明
On some typical commercial high pressure polyethylenes, [η] (145°C, dioctyl adipate) was measured, and assuming them as [η] θ, the expansion factors (α3η≡ [η] (75°C, xylene) / [η] θ) were determined.<BR>Vessel-type polyethylenes generally showed a tendency to have larger α3η than that of tubular-type polyethylenes and this tendency was more remarkable for the samples fractionated by molecular weight.<BR>The expansion factor of linear polyethylene was smaller than that of high pressure polyethylenes and it hardly varied with molecular weight. As the addition of long-chain branchings by gamma ray irradiation did not vary the value of α3η of linear polyethylene, it was considered that large α3η for high pressure polyethylenes is not due to the presence of long-chain branching itself but due to the presence of “complicated long-chain branchings having many short-chain branchings” . Expansion factors of the high pressure polyethylenes increased with molecular weight and this result was considered to be caused by the fact that the amount of complicated long-chain branchings increases with increasing molecular weight. MI- [η] correlation could be explained by two effects which are the effect of degree of long-chain branching itself on the melt viscosity-solution viscosity correlation and the change of excluded volume effect due to the presence of complicated long-chain branchings.
収録刊行物
-
- 高分子化學
-
高分子化學 28 (312), 312-320, 1971
公益社団法人 高分子学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681497563904
-
- NII論文ID
- 130003835987
-
- ISSN
- 18848079
- 00232556
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可