重合過程を利用した高分子結晶の形態制御に関する研究　第４報　ポリ（ｐ‐オキシベンゾイル）ウィスカーの生成過程における重合度変化

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • Studues on morphology conrtrol of polymer crystals during polymerization IV. Molecular weight change during poly(p-oxybenzoyl) whisker formation.
  • ポリ p オキシベンゾイル ウィスカー ノ セイセイ カテイ ニ オケル ジュ

この論文をさがす

説明

Molecular weight changes during poly (p-oxybenzoyl) whisker formation from p-acetoxybenzoic acid in liquid paraffin were studied. Our electron microscope observation suggestd that the needle crystals in the very early stage of polymerization consist of stacks of oligomer lamellae. Here, the degree of polymerization of precipitated oligomers was found to be about 8, from analysis of oligomers dissolved in liquid paraffin by HPLC method. Furthermore, transesterification in the interlamellar regions starts as soon as crystals precipitate. The average DP of whiskers obtained with 3 min after crystal precipitation increases from 8 to 48. These crystals show fibrillation by crushing of whiskers in liquid nitrogen or etching in KOH solution. This fact indicates that reorganization into extended chain crystals occurs accompanied by the increase of DP. On the other hand, DP of the eventual whiskers increased by 1860. That is, the average molecular length exceeds 1μm. The formation of such high molecular weight polymers in the solid state polymerization is caused by the closely packed structure of the end groups.

収録刊行物

  • 高分子論文集

    高分子論文集 47 (7), 583-589, 1990

    公益社団法人 高分子学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ