難燃剤テトラブロモビスフェノールＡ‐ビス（２，３‐ジブロモプロピル）エーテル添加ポリプロピレン組成物におけるブルーミング現象メカニズムの解明　２　　難燃剤の結晶形態の違いによるブルーミングメカニズム

DOI

書誌事項

タイトル別名
  • Effect of Crystalline Form of Flame-Retardant on Blooming Mechanism.

説明

The EVA content necessary to suppress the blooming in sheetings was determined. The content was higher than that in the case of injection moldings, and the appropriate blooming acceleration temperature was around 70°C being higher than that in the case of injection moldings. This is assumed to be because the amorphous region of PP in sheetings which can dissolve TBA-DB is less than that in injection moldings and because there exist skin layers where the transportation rate of additives is low in injection moldings. When a stimulation is applied to a part of surface of injection molding or sheeting by, for example, sucking operation and handling just after processing, a blooming generates at the part, and the necessary EVA content was determined to suppress it. TBA-DB has crystalline and amorphous forms, and the crystalline substance was observed as blooms while the transparent amorphous substance was not observed. Whether the crystalline substance is formed in the processed article or not unitarily determines the generation of blooming. When a stimulation was applied to the surface of a processed article at temperatures above the softening temperature of the amorphous substance (40°C), crystallization nuclei generated on it. By aging the processed article at temperatures above 40°C, the nuclei absorbed the amorphous substance, grew and became to be observed as blooms.

収録刊行物

  • 高分子論文集

    高分子論文集 58 (9), 462-471, 2001

    公益社団法人 高分子学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390282681500055808
  • NII論文ID
    130004035504
  • DOI
    10.1295/koron.58.462
  • ISSN
    18815685
    03862186
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ