- Properties of Multiwall Carbon Nanotubes/Polystyrene-block-polybutadiene-block-polystyrene Composites
- 各種多層カーボンナノチューブ/ポリスチレン-block-ポリブタジエン-block-ポリスチレン複合物の諸物性
- カクシュ タソウ カーボンナノチューブ ポリスチレン block ポリブタジエン block ポリスチレン フクゴウブツ ノ ショ ブッセイ
この論文をさがす
抄録
The influence of characteristics of multiwall carbon nanotubes (MWCNTs) on the properties of polystyrene-block-polybutadiene-block-polystyrene (SBS) / MWCNT composites was investigated. The three types of MWCNTs which have a different in the degrees of graphitization (CNT-1; φ 87 nm, G/D ratio 9.09 and CNT-2; φ 87 nm, G/D ratio 0.78) and the diameter (CNT-3; φ 10-15 nm) were used as a filler. The composites were prepared using a mixing roll. The tensile moduli of the composites were improved even at low concentration of MWCNTs. The volume resistivity of the composite compounded with CNT-1 was markedly decreased at the lowest content of MWCNT, 4.4 vol%. The new peak of the loss tangent (tanδ) was observed around –10 °C in the temperature dependence of tanδ for the composites compounded with CNT-1. These results suggest that another relaxation system in SBS was newly formed by compounding CNT-1.
収録刊行物
-
- 日本ゴム協会誌
-
日本ゴム協会誌 83 (8), 258-263, 2010
一般社団法人 日本ゴム協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681539996928
-
- NII論文ID
- 10026554870
-
- NII書誌ID
- AN00269207
-
- COI
- 1:CAS:528:DC%2BC3cXhtlegtb3K
-
- ISSN
- 18840442
- 0029022X
-
- NDL書誌ID
- 10775619
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可