- Dependences of Grain Size and Strain-Rate on Deformation Behavior of Commercial Purity Titanium Processed by Multi-Directional Forging
- タジク タンゾウ カコウ オ ホドコシタ コウギョウヨウ ジュンチタン ノ ヘンケイ キョドウ ノ ケッショウ リュウケイ イソンセイ ト ヒズミ ソクド イソンセイ
この論文をさがす
抄録
<p>Strain-rate dependencies of deformation behavior of commercial purity titanium specimens having different grain sizes were systematically investigated. Ultrafine-grained titanium with an average grain size of 0.07 µm (UFG-Ti) fabricated by multi-directional forging followed by conventional thermo-mechanical processing, and fine-grained (FG-Ti) and coarse-grained (CG-Ti) specimens with an average grain sizes of 0.8 µm and 12 µm attained by its, respectively, annealing at 773 K and 973 K for 1.8 ks were prepared. The FG- and UFG-Ti specimens exhibited strong strain-rate dependence of 0.2% proof stress, while that of CG-Ti ones were almost constant regardless of applied strain-rate. In-situ X-ray diffraction measurements during tensile tests were also conducted at synchrotron radiation facility, SPring-8. Using the modified Williamson-Hall and the modified Warren-Averbach methods, the activated slip systems and change in dislocation density during deformation were estimated. As a result, it was found that <a> and <c+a> slips were activated in FG- and UFG-Ti specimens. On the other hand, the activation of <c+a> slip was never observed in the CG-Ti ones. It can be, thus, concluded that the different strain-rate dependency of deformation behaviors of specimens with different grain sizes were ascribed to the difference in the deformation mechanisms.</p>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 83 (12), 465-473, 2019-12-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282752372799616
-
- NII論文ID
- 130007751059
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 030105862
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可