硫酸塩浴からの低熱膨張型電析Fe-Niインバー合金の形成に及ぼす液組成と添加剤の影響

DOI DOI Web Site Web Site Web Site 被引用文献5件 参考文献25件 オープンアクセス

書誌事項

タイトル別名
  • Effects of Electrolyte Composition and Additives on the Formation of Invar Fe-Ni Alloys with Low Thermal Expansion Electrodeposited from Sulfate Bath
  • リュウサンエンヨク カラ ノ テイネツ ボウチョウガタデンセキFe-Ni インバー ゴウキン ノ ケイセイ ニ オヨボス エキ ソセイ ト テンカザイ ノ エイキョウ

この論文をさがす

説明

<p>The effects of solution composition and additives on the formation of electrodeposited invar Fe-Ni alloys with low thermal expansion was investigated. In all the solutions, with increasing the current density from 10 A·m–2, the Ni content in deposits significantly decreased and showed the anomalous codeposition in which electrochemically less noble Fe deposits preferentially. With increasing current density further, Fe deposition reached the diffusion limitation of Fe2+ ions, as a result, the Ni content in deposits increased with current density. The current density for initiating to increase the Ni content in deposits shifted to higher value with increasing the concentration of Fe2+ ions because of increase in diffusion-limited current density of Fe. With increasing the concentration of malonic acid, the current density region in which the Ni deposition was suppressed, extended and the potential which Fe deposition reached to the diffusion limitation of Fe2+ ions shifted to the less noble direction. As a result, the curve which showed the relationship between the Ni content in deposits and current density, shifted to higher current density region with increasing the malonic acid. The current efficiency for alloy deposition greatly decreased due to promotion of hydrogen evolution with the concentration of malonic acid above 0.05 mol·dm–3. The Ni content in deposits significantly increased with thiourea. With boric acid, the Ni content in deposits somewhat increased in the lower current density region. With both boric acid and saccharin, the invar alloy of Fe-36 mass% Ni was obtained in the wider current density region.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 104 (10), 585-593, 2018

    一般社団法人 日本鉄鋼協会

被引用文献 (5)*注記

もっと見る

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ