Dielectric properties of MgTi<sub>1−</sub><i><sub>x</sub></i>(Zn<sub>1/3</sub>B<sub>2/3</sub>)<i><sub>x</sub></i>O<sub>3</sub> (B = Nb<sup>5+</sup>, Ta<sup>5+</sup>) ceramics at microwave frequencies

DOI Web Site 参考文献3件
  • KIM Jae Min
    Department of Materials Engineering, Kyonggi University
  • KIM Eung Soo
    Department of Materials Engineering, Kyonggi University

この論文をさがす

説明

<p>Microwave dielectric properties of MgTi1−x(Zn1/3B2/3)xO3 (B = Nb5+, Ta5+, 0.025 ≤ x ≤ 0.125) were investigated based on their structural characteristics and the electronegativity difference of the constituent ions. For the specimens of MgTi1−x(Zn1/3Nb2/3)xO3, a single phase of the rhombohedral ilmenite structure appeared for the entire range of compositions (0.025 ≤ x ≤ 0.125), while MgTi1−x(Zn1/3Ta2/3)xO3 showed a single phase of ilmenite structure up to x = 0.075, and then MgTi2O5 was detected as a secondary phase on further substitution of (Zn1/3Ta2/3)4+ at Ti4+-site of MgTiO3. Quality factor value increased with the electronegativity difference up to an electronegativity difference of 2.015 and was dependent on the degree of covalent character of the bond. Temperature coefficient of resonant frequency decreased with an increase in oxygen octahedral distortion. Dielectric constant of the specimens did not exhibit any remarkable change with the substitution of (Zn1/3B2/3)4+ at Ti4+-site of MgTiO3.</p>

収録刊行物

参考文献 (3)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ