Inhibition Effect of Ti(C,N) Particle Dispersion on Grain Growth of WC-Co Cemented Carbide

DOI Web Site Web Site 被引用文献1件 参考文献21件

この論文をさがす

抄録

<p>The WC-Co cemented carbides with the addition of Ti(C,N) base particles with different sizes were fabricated by liquid phase sintering and their microstructures were mainly investigated in detail comparing the microstructure of the alloys with VC and Cr3C2 addition. It was found that the WC grain growth was more strongly inhibited with increasing Ti(C,N) content and with decreasing Ti(C,N) particle size. The degree of inhibition by the addition of Ti(C,N) particle with about 0.1 µm size was lower than that of VC addition and was almost same as that Cr3C2 of addition. Considering the results about the relationship between WC grain size and Ti(C,N) particle size and the analysis of Co phase composition, it was seen that the mechanism of grain growth inhibition by the addition of Ti(C,N) particles was the pinning (Zener) effect by the second phase particle, which was different from the mechanism for the addition of VC and Cr3C2 reported previously. The case that one Ti(C,N) particle contacts plural WC grains was often observed, so that the pinning effect was considered to work by many Ti(C,N) particles neighboring one WC grain. The very important result that the pinning effect by Ti(C,N) addition enable to develop the new type of ultra-fine cemented carbide was obtained in this study.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Jpn. Soc. Powder Powder Metallurgy 65 (2018) 91–98.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 60 (5), 785-792, 2019-05-01

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (21)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ