- Effects of Fine Alumina Addition and Sintering Temperature on Mechanical Properties of Alumina-Magnesia Monolithic Refractories
- アルミナ-マグネシアシツ フテイケイ タイカブツ ノ キカイテキ トクセイ ニ オヨボス ビフン テンカ オヨビ ショウセイ オンド ノ エイキョウ
この論文をさがす
抄録
<p>Alumina-magnesia monolithic refractories are mainly used to line the inner wall of steel ladles. The refractories are damaged by the thermal shock while using on its wall and the spalling of them occurs. Therefore, it is very important to evaluate the thermal shock resistance of refractories. The effective fracture energy (γeff) is known as the parameter which affects to the thermal shock resistance. The objective of this study is to identify the effect of adding fine particles on the γeff. The samples were prepared by changing the fraction of fine alumina (average particle size is 3.4 µm) against coarse alumina (average particle size is 550 µm) and the effect of adding fine particles on the γeff was evaluated. The γeff was measured by Work of Fracture method. The value of γeff was enhanced to a maximum when the fine alumina fraction was 20-30 mass%. The reason could be explained by the apparent porosity and the roughness of the surface. Adding appropriate amount of fine alumina brought lower apparent porosity and rougher surface, leading to higher γeff.</p>
収録刊行物
-
- 材料
-
材料 68 (7), 559-563, 2019-07-15
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282763130378496
-
- NII論文ID
- 130007681640
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 029875576
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可