- Coarsening of Plate-Like C15–Al<sub>2</sub>Ca Precipitates in a Mg–Al–Ca Alloy
- Mg-Al-Ca合金における平盤状C15-Al₂Ca析出相の粗大化過程
- Mg-Al-Ca ゴウキン ニ オケル ヘイバンジョウ C15-Al ₂ Ca セキシュツソウ ノ ソダイカ カテイ
この論文をさがす
説明
<p>The coarsening kinetics of the fine C15–Al2Ca Laves phase with a plate-like morphology, which precipitated within the primary α-Mg grains, were investigated for the Mg–5Al–1.5Ca alloy aged at 523 K. The Al2Ca precipitate coarsened with remaining coherency in the aging time below 300 h, and the quantitative relationship was obtained between precipitate length, l, and aging time, t, as follows; l ∝ t 0.23. By contrast, the α/C15 coherent interface turned to the semi-coherent one by the introduction of misfit dislocations on the planar surface of the precipitates in the aging time above 300 h, which resulted in the promotion of Al2Ca coarsening. The Al2Ca phase was deduced to precipitate through a nucleation and growth mechanism rather than spinodal decomposition, and its coarsening was explained using the terrace-ledge-kink mechanism. The aspect ratio of Al2Ca precipitates was predominantly decided by the aging temperature, and it decreased at higher aging temperatures.</p>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 83 (8), 282-287, 2019-08-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282763131482496
-
- NII論文ID
- 130007683517
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 029922701
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可