Fatigue Properties of SUS316LN Stainless Steel Sheet with Heterogeneous Nano-structure Developed by Heavy Cold Rolling
-
- Kobayashi Masakazu
- Department of Mechanical Engineering, Toyohashi University of Technology
-
- Iwama Shouhei
- Graduate Student, Department of Mechanical Engineering, Toyohashi University of Technology
-
- Watanabe Chihiro
- Faculty of Mechanical Engineering, Kanazawa University
-
- Aoyagi Yoshiteru
- Department of Finemechanics, Tohoku University
-
- Miura Hiromi
- Department of Mechanical Engineering, Toyohashi University of Technology
Bibliographic Information
- Other Title
-
- 強冷間圧延によりヘテロナノ組織を発達させたSUS316LNステンレス鋼板材の疲労特性
- キョウ レイカン アツエン ニ ヨリ ヘテロナノ ソシキ オ ハッタツ サセタ SUS316LN ステンレス コウバンザイ ノ ヒロウ トクセイ
Search this article
Abstract
<p>Fatigue behaviors of SUS316LN austenitic stainless steel with heterogeneous nano-structure developed by heavy cold rolling have been investigated in this study. The tensile strength and the elongation to fracture in the heterogeneous nano-structure SUS316LN were 1552 MPa and 10%, respectively. The fatigue strength of the heterogeneous nano-structure SUS316LN, which was defined at 107 cycles, reached double of fatigue strength of conventional austenitic stainless steels. The improvement of fatigue strength can be connected with ultimate tensile strength in the heterogeneous nano-structure SUS316LN. Fish-eye fractures, in which crack initiated at Al2O3 inclusions, were clearly observed on the fracture surfaces. The crack propagation rate was measured based on the striation intervals on fracture surface, the analysis of crack propagation rate revealed that the cracks tend to propagate difficult to sheet thickness direction due to lamella structure whose grain boundaries are low misorientation angles. The fatigue lives before and after crack initiation were also estimated by using the number of cycles at fracture and the crack propagation rate. It was found that most of fatigue life was spent before crack initiation. Therefore, fatigue strength would be able to improve by reducing the number and size of inclusion particles.</p>
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 106 (7), 507-516, 2020
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390285300170653824
-
- NII Article ID
- 130007866392
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 030548364
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed