- Evolution of crystal orientation distribution in thickness direction of spun A1050 disk
説明
<p>This study clarified the evolution of crystal orientation distribution in thickness direction of spun A1050 disk using electron back scatter diffraction pattern analysis. This study defined texture-I, II, and III as follows. The texture-I was rotated 20° around <111> from the Cu texture. The texture II was rotated 5° around its <110> from the Cu texture. The texture III was rotated 10° around its <110> from the texture-I. When the blank disk had a sandwich-type layer structure in thickness direction: Cu-I-Cu, the analysis results indicated the following texture evolution. In early passes, the structure was Cu-I-Cu. In later passes, the structures at wall and in the vicinity of the edge of the workpiece were Cu-II-II and Cu-III-III, respectively. In middle passes, the structure had a complex-type of three structures. These results suggest that the crystal orientation changed in the approximately two thirds in thickness from mandrel side by conventional spinning.</p>
収録刊行物
-
- 年次大会
-
年次大会 2020 (0), J03113-, 2020
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390287462801090944
-
- NII論文ID
- 130008003449
-
- ISSN
- 24242667
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可