Structure of Corrosion Product Formed on Carbon Steel Covered with NiSO<sub>4</sub>-Added Resin Coating under Sulfuric Acid Mist Environment Containing Chloride

DOI DOI IR (HANDLE) IR (HANDLE) Web Site View 3 Remaining Hide 3 Citations 16 References Open Access
  • Hayashida Shota
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
  • Takahashi Masamitsu
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University Nagase & Co., LTD.
  • Deguchi Hiroshi
    Kansai Electric Power Co., Inc.
  • Tsuchiya Hiroaki
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
  • Hanaki Koushu
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University Kyoto Materials Co., Ltd.
  • Yamashita Masato
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University Kyoto Materials Co., Ltd.
  • Fujimoto Shinji
    Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University

Bibliographic Information

Other Title
  • 塩化物を含む硫酸ミスト環境においてNiSO<sub>4</sub>含有樹脂被覆炭素鋼に形成した腐食生成物の構造
  • 塩化物を含む硫酸ミスト環境においてNiSO4含有樹脂被覆炭素鋼に形成した腐食生成物の構造
  • エンカブツ オ フクム リュウサン ミスト カンキョウ ニ オイテ NiSO ₄ ガンユウ ジュシ ヒフク タンソコウ ニ ケイセイ シタ フショク セイセイブツ ノ コウゾウ
  • Structure of Corrosion Product Formed on Carbon Steel Covered with NiSO₄-Added Resin Coating under Sulfuric Acid Mist Environment Containing Chloride

Search this article

Description

<p>Corrosion resistance of carbon steel covered with resin coating containing nickel sulfate has been evaluated under chloride and sulfuric acid mist environment. The structure of corrosion products formed on steel surface was investigated by XRD and XAFS analyses using synchrotron radiation. Nickel sulfate promoted the formation of goethite and akaganeite. It was considered that this akaganeite was not tetragonal β-FeOOH but monoclinic akaganeite containing nickel.</p><p> </p><p>This Paper was Originally Published in Japanese in Zairyo-to-Kankyo 69 (2020) 148–153.</p>

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 62 (6), 781-787, 2021-06-01

    The Japan Institute of Metals and Materials

Citations (3)*help

See more

References(16)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top