Tensile Deformation of Si Single Crystals with Easy Glide Orientation

DOI Web Site Web Site 被引用文献1件 参考文献26件 オープンアクセス
  • Suzuki Tubasa
    Department of Materials Science and Engineering, Kyushu University
  • Tanaka Masaki
    Department of Materials, Kyushu University Centre for Elements Strategy Initiative for Structural Materials, Kyoto University
  • Morikawa Tatsuya
    Department of Materials, Kyushu University
  • Fujise Jun
    Advanced Evaluation and Technology Development Department, SUMCO Corporation
  • Ono Toshiaki
    Advanced Evaluation and Technology Development Department, SUMCO Corporation

この論文をさがす

説明

<p>Silicon single crystals were deformed in tensile tests along the [134] direction between 1173 K and 1373 K. The yield point phenomenon was observed in the specimens deformed below 1273 K, while a continuous yield was observed in the specimens deformed above 1323 K. The values of work-hardening rate in stage II were the same as those reported in other single crystals. Orientation maps of the specimen obtained by using electron backscattered electron diffraction method indicated that stage II starts before the Schmid factor of the secondary slip system became larger than that of the primary slip system. Because of the constraint due to the gripping of the test piece, kink bands are formed during stage I before the onset of stage II, and then the stress state becomes non-uniaxial. This suggests that the formation of kink bands triggers the activation of the secondary, i.e., conjugate slip system to increase the resolved shear stress on the conjugate slip systems.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 62 (7), 975-981, 2021-07-01

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (26)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ