エポキシ樹脂用潜在性硬化剤としての熱カチオン重合開始剤の構造と特性

DOI Web Site Web Site 参考文献17件

書誌事項

タイトル別名
  • Structure and Properties of Thermal Cationic Polymerization Initiator as a Latent Curing Agent for Epoxy Resin
  • エポキシ ジュシヨウ センザイセイ コウカザイ ト シテ ノ ネツ カチオン ジュウゴウ カイシザイ ノ コウゾウ ト トクセイ

この論文をさがす

説明

<p>In recent years, the thermal cationic polymerization initiator（ or the thermal acid generator） is expanding its use as a latent curing agent for epoxy resin mainly in the electrical and electronic fields due to several advantages including the good storage stability at room temperature, the short-time curing at relatively low temperatures around 100 ℃, and the easiness to handle. The major type cationic initiator available in the market is the combination of monoarylsulfonium cation and antimony hexafluoride anion（ SbF6-）. Because of the toxicity of heavy metal（ Sb）, however, phosphorous hexafluoride anion（ PF6-）, tetrakis（ pentafluorophenyl） borate anion（ TFPB-）, and（ Rf）nP-F6-n, in which some of the fluorine of PF6- are replaced with perfluoroalkyl groups, are also applied. TFPB- and（ Rf）nP-F6-n have the polymerization activity comparable to SbF6- although PF6- is less active. Other typical cationic components are thiophenium, quaternary anilinium, and diaryliodonium cations. As a unique type initiator different from the above salt type ones, there is a complex catalyst that combines Al-complex and alkoxysilane. Taking CAS registration number as identification mainly for the thermal cationic polymerization initiators commercially available, the article focuses on reviewing the relationship between the molecular structure and the epoxide polymerization ability of the cationic initiator.</p>

収録刊行物

参考文献 (17)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ